NANJING, JIANGSU, CHINA, January 10, 2024 /EINPresswire.com/ -- In this work, researchers from South China University of Technology (SCUT) successfully synthesized a Cr3+ doped perovskite-type LaAlO3 mechanoluminescence (ML) phosphor. Combined with persistent luminescence, diffuse reflectance, preheating method, thermoluminescence and corresponding ML analysis, the inherent mechanism of self-recoverable ML has been discussed in detail, which depends more on the piezoelectricity of the non-centrosymmetric LaAlO3: Cr3+. Our findings may partly lay the foundation for uncovering the mask of the NIR ML mechanism.

Mechanoluminescence (ML) located within the near infrared (NIR) spectral range may have hold promising applications in in-situ and real-time biomechanical imaging. This is due to the better spatial resolution and penetration depth of the biological tissues, lower optical loss and the avoidance of autofluorescence. Historically, rare earth ions have been predominantly employed as activators in ML materials. However, adjusting the emissions of rare earth ions, especially RE3+, poses challenges, thereby limiting the practical application of NIR MLs. Therefore, the transition metal ions activated systems have been favored by more and more researchers.

Previously, Puxian Xiong and colleagues have reported a self-recoverable NIR ML material in gallate by using Cr3+ ions as the emission center for the first time.

“Indeed, LiGa5O8:Cr3+ presents good ML repeatability and does not require pre-irradiation process, but the intrinsic ML mechanisms are still not entirely clear,” says Xiong. “In particular, whether the remanent carriers occupied lattice traps can affect the ML repeatability is unclear.”

As is generally known, the preheating method is one of the most effective ways to remove the remanent carriers. In a new study published in Advanced Powder Materials, the team integrated the preheating method with corresponding ML results. “This work intends for actualizing the analysis of the ML mechanism through eliminating the influences of stored carriers,” shares Xiong, who serves as co-corresponding author of the study.

In all, Cr3+ ions doped perovskite-type LaAlO3 ML phosphor is successfully synthesized by a traditional high-temperature solid-sate reaction method in air. Combined with photoluminescence, persistent luminescence, diffuse reflectance and thermoluminescence characterizations, the inherent ML mechanism was discussed in detail by the authors.

“We observed that ML in LaAlO3: Cr3+ is self-recoverable, which is obviously different from the trap-controlled ML compounds (requiring UV light for pre-irradiation). Based on the preheating method and corresponding ML analysis, such self-recoverable ML depends more on the piezoelectricity of the non-centrosymmetric LaAlO3: Cr3+,” shares Xiong.

Under mechanical stimuli, a strong piezoelectric field is built within the compound, which is large enough to generate electronically excited states of the Cr3+ ions, subsequently resulting in ML. This luminescence is featured with self-recoverability, implying that the compound can be applied to different applications.

“We further demonstrated great potential application prospects for the ML Bioimaging, anti-counterfeiting and information encryption field with the encoding and decoding of ASCII code,” adds Xiong.

Reference
Funder: We gratefully acknowledge the financial support from the National Natural Science Foundation of China (No. 52202003), Guangdong Basic and Applied Basic Research Foundation (No. 2023A1515011893), State Key Laboratory of Powder Metallurgy, Central South University, Changsha, China (No. Sklpm-KF-27) and Guangzhou Basic and Applied Basic Research Foundation (No. SL2022A04J00746).
DOI: 10.1016/j.apmate.2023.100165
Original URL: https://doi.org/10.1016/j.apmate.2023.100165

Lucy Wang
BioDesign Research
+86 177 0518 5080
email us here

Legal Disclaimer:

EIN Presswire provides this news content "as is" without warranty of any kind. We do not accept any responsibility or liability for the accuracy, content, images, videos, licenses, completeness, legality, or reliability of the information contained in this article. If you have any complaints or copyright issues related to this article, kindly contact the author above.